Modified silane adhesive two

• Overview
• Product Description
• Application
• Character
• Product Parameters
• Packaging & Shipping

Overview

Basic Info.

Model NO.	HM-MS7210
Composition	Organic Material
Morphology	Solvent
Material	Silicone
Classification	Room Curing
Main Agent Composition	Natural Polymer
Characteristic	Weatherability
Promoter Composition	Curing Agent
EINECS	N/A
Formula	N/A
CAS No.	N/A
Transport Package	box
Specification	N/A
Trademark	Howell
Origin	China
Production Capacity	100000

Product Description

HM-MS7210 is a two-component adhesive based on silane-terminated polyether polymer. It is neutral and has good thixotropic properties and initial strength. Component A and Component B can solidify within a certain period of time after being mixed. An elastomer is formed that meets customer requirements for rapid cure, and increasing the temperature can also speed up the cure. Odorless, solvent-free, isocyanate-free and PVC-free.

This product has comprehensive properties of elastic sealing and bonding. The cured product can be painted, electrophoresed, and baked at high temperatures. It is suitable for parts that require elastic sealing and a certain bonding strength.

•Bonding of logistics vehicle skin and frame
•Body structure bonding via electrophoresis painting
•Structural bonding in rail transit, elevator and other industries

▪ Fast one-piece solidification, high strength
▪ High temperature resistant electrophoresis process
▪ Surface can be painted
• Environmentally friendly, free of solvents, isocyanates, and halogens

Adhesive liquid properties before curing

Curing properties *The above data are typical values tested at (23±2)ºC and (50±5)% humidity. The actual curing speed will vary with temperature and humidity.

Properties after curing
Performance after high temperature (180ºC50min)

400ml (4:1) Cartridge

Product Description Application Character Product Parameters

Mixing ratio (volume ratio)	4:1
Mixed (A/B) color	black (black/beige)
Appearance after mixing (A/B)	Thixotropic paste (thixotropic/thixotropic)
After mixing (A/B) specific gravity	1.24 (1.28/1.05)

Surface drying time (min)	30
Gel time (min)	50

Tensile strength (MPa)	3.0
Elongation at break (%)	270
Hardness (Shore A)	45
Shear strength (MPa)	3.5
Working temperature range (ºC)	-45~120
Short-term temperature resistance (ºC)	180

Tensile strength (MPa)	4.2
Elongation at break (%)	280
Hardness (Shore A)	45
Shear strength (MPa)	3.5